Injection molding is a cornerstone of modern manufacturing, enabling the mass production of precise, complex plastic parts. But behind every successful injection-molded component lies a well-designed mold. A poorly designed mold can lead to defects, increased production costs, and delayed timelines—while a thoughtfully engineered one ensures efficiency, quality, and scalability. In this blog, we’ll explore the fundamentals of injection mold design, from core principles to actionable best practices.
The Basics: What is Injection Mold Design?
An injection mold is a precision tool that shapes molten plastic into a desired form. It consists of two main halves: the **cavity** (which forms the outer surface of the part) and the **core** (which shapes the inner surface). When closed, these halves create a cavity that matches the part’s design. The mold also includes systems for feeding plastic (sprue and runners), cooling the part, and ejecting the finished component.
Mold design is the process of engineering this tool to meet the part’s specifications, production volume, and material requirements. It’s a blend of engineering, material science, and problem-solving—critical for achieving consistent, high-quality parts.
Key Principles of Effective Injection Mold Design
1. Design for Manufacturability (DFM)
The part’s design and the mold’s design are inseparable. Before finalizing a mold, ensure the part is optimized for injection molding:
Wall thickness: Aim for uniform thickness (typically 1–3mm) to avoid warping or uneven cooling. Thicker sections can trap air or cause sink marks; thinner areas may not fill properly.
Draft angles: Add slight angles (0.5°–2°) to vertical surfaces to help eject the part from the mold. Without draft, parts can stick, damaging both the mold and the component.
Undercuts: Avoid features like grooves or protrusions that prevent the part from releasing (e.g., a “lip” inside a cup). If undercuts are necessary, use slides or lifters in the mold—though these add complexity and cost.
2. Material Compatibility
Different plastics behave differently in the mold, so design must align with the chosen material:
Viscosity: Low-viscosity materials (e.g., PP) flow easily and require less injection pressure; high-viscosity materials (e.g., PC) need more pressure and larger gates to fill the mold.
Shrinkage: All plastics shrink as they cool. For example, PP shrinks 1.5–2.5%, while ABS shrinks 0.4–0.7%. The mold must account for this to ensure the final part meets尺寸 (dimensional) specs.
Heat sensitivity: Some materials (e.g., PVC) degrade at high temperatures, requiring cooler mold temperatures and faster cycles.
3. Gate Design
The gate is the opening through which molten plastic enters the mold cavity. Its size, shape, and location directly impact part quality:
Location: Place gates where they minimize flow lines (visible streaks) and ensure even filling. For large parts, multiple gates may be needed to avoid air traps.
Size: A gate that’s too small causes high pressure and shear, damaging the material; too large leaves excess plastic (a “gate vestige”) that requires post-processing.
Type: Common gate types include:
Edge gates: Simple, low-cost, ideal for flat parts.
Submarine gates: Hidden under the part, reducing post-processing.
Hot runners: Reusable, heated channels that eliminate waste (no cold runner to trim), suited for high-volume production.
4. Cooling System Design
Proper cooling is critical for cycle time and part stability. Molten plastic must cool evenly to prevent warping, sinks, or internal stresses:
Cooling channels: Drill channels in the mold (typically 8–12mm diameter) to circulate water or oil. Place them 1–2x the channel diameter from the cavity surface for efficient heat transfer.
Uniformity: Ensure channels follow the part’s shape. For example, a curved part needs curved channels to avoid uneven cooling.
Flow rate: Fast water flow removes heat faster, reducing cycle time—but balance with pressure to avoid channel erosion.
5. Ejection System
Once cooled, the part must be safely ejected from the mold. Ejectors (pins, plates, or sleeves) should:
Distribute force evenly: Avoid bending or marking the part. For large parts, use multiple ejector pins.
Align with cooling: Ejectors should not block cooling channels, as this creates hot spots.
Be accessible: Ejector pins need clearance for movement and easy maintenance.
Common Mistakes to Avoid
Overcomplicating the mold: Adding unnecessary features (e.g., complex slides) increases cost and reduces reliability.
Ignoring shrinkage: Failing to account for material shrinkage leads to parts that are too small or misshapen.
Poor venting: Trapped air in the mold causes burns, incomplete filling, or voids. Add vents (0.02–0.05mm deep) at cavity edges to release air.
Final Thoughts
Injection mold design is a balance of art and science—requiring deep knowledge of materials, manufacturing processes, and part requirements. A well-designed mold not only produces high-quality parts but also reduces waste, shortens cycle times, and lowers long-term costs. Whether you’re prototyping a small component or scaling to mass production, investing in thoughtful mold design is the foundation of success in injection molding.
Kingchen Machinery have a complete production line from mold design to manufacturing. If you are looking for a factory to produce your own personalized injection molds or rubber molds, please feel free to contact us to obtain suitable solutions and quotations.